PUR-Ether/PPDI Ultralast™ PE952 CHEMTURU USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | CHEMTURU USA/Ultralast™ PE952 |
|---|---|---|---|
| Dynamic Properties | StorageModulus:120°C | 2.97E+08 dynes/cm² | |
| TangentDelta:30°C | 0.0250 | ||
| TangentDelta:120°C | 0.0380 | ||
| StorageModulus:30°C | 4.53E+08 dynes/cm² |
| hardness | Test Condition | Test Method | CHEMTURU USA/Ultralast™ PE952 |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 43to45 |
| 邵氏A | ASTM D2240 | 95to97 |
| film | Test Condition | Test Method | CHEMTURU USA/Ultralast™ PE952 |
|---|---|---|---|
| Tear resistance of pants | ASTM D1938 | 67.1 N/mm |
| Mechanical properties | Test Condition | Test Method | CHEMTURU USA/Ultralast™ PE952 |
|---|---|---|---|
| Wear resistance - DIN | DIN 53516 | 27.0 mm³ | |
| Flexural modulus | ASTM D790 | 89.5 MPa |
| physical property | Test Condition | Test Method | CHEMTURU USA/Ultralast™ PE952 |
|---|---|---|---|
| Shrinkage rate | TD:24小时 | ASTM D955 | 2.0 % |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 5.0to15 g/10min |
| density | ASTM D792 | 1.10 g/cm³ | |
| Shrinkage rate | MD:24小时 | ASTM D955 | 2.0 % |
| elastomer | Test Condition | Test Method | CHEMTURU USA/Ultralast™ PE952 |
|---|---|---|---|
| elongation | 断裂 | ASTM D412 | 660 % |
| tear strength | 开裂 | ASTM D470 | 44 kN/m |
| Shore hardness | ASTM D2632 | 63 % | |
| tensile strength | ASTM D412 | 36.5 MPa | |
| compression set | 70°C,22hr | ASTM D395B | 35 % |
| tear strength | 开裂2 | ASTM D470 | 34 kN/m |
| tensile strength | 100%应变 | ASTM D412 | 12.4 MPa |
| tear strength | 开裂3 | ASTM D470 | 35 kN/m |
| Thermal performance | Test Condition | Test Method | CHEMTURU USA/Ultralast™ PE952 |
|---|---|---|---|
| vicat | ASTM D1525 | 166 °C | |
| Glass Transition Temperature | -53.0 °C |