Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PLA F 1137 FKuR Kunststoff GmbH
--
Film, bag
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | FKuR Kunststoff GmbH/F 1137 |
---|---|---|---|
Impact strength of simply supported beam without notch | ISO 179/1eU | 无断裂 | |
Charpy Notched Impact Strength | ISO 179/1eA | 无断裂 |
film | Test Condition | Test Method | FKuR Kunststoff GmbH/F 1137 |
---|---|---|---|
elongation | TD:屈服,20µm | ISO 527-3 | 460 % |
tensile strength | TD:屈服,20µm | ISO 527-3 | 25.0 MPa |
TD:断裂,20µm | ISO 527-3 | 24.0 MPa | |
elongation | TD:断裂,20µm | ISO 527-3 | 460 % |
Tensile modulus | MD:20µm | ISO 527-3 | 515 MPa |
tear strength | Elmendorf-MD:20.0µm | ISO 6383-2 | 100 kN/m |
tensile strength | MD:屈服,20µm | ISO 527-3 | 37.0 MPa |
MD:断裂,20µm | ISO 527-3 | 36.0 MPa | |
tear strength | Elmendorf-TD:20.0µm | ISO 6383-2 | 290 kN/m |
film thickness | 20 µm | ||
elongation | MD:屈服,20µm | ISO 527-3 | 290 % |
Tensile modulus | TD:20µm | ISO 527-3 | 420 MPa |
elongation | MD:断裂,20µm | ISO 527-3 | 290 % |
Mechanical properties | Test Condition | Test Method | FKuR Kunststoff GmbH/F 1137 |
---|---|---|---|
tensile strength | 断裂 | ISO 527-2 | 13.8 MPa |
Tensile strain | 断裂 | ISO 527-2 | 430 % |
bending strength | 3.5%应变 | ISO 178 | 11.5 MPa |
Tensile modulus | ISO 527-2 | 310 MPa | |
tensile strength | 屈服 | ISO 527-2 | 15.5 MPa |
Fracture bending strain | ISO 178 | NoBreak | |
Flexural modulus | ISO 178 | 305 MPa | |
Tensile strain change rate | ISO 527 | 420 % |
physical property | Test Condition | Test Method | FKuR Kunststoff GmbH/F 1137 |
---|---|---|---|
Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 1.50to3.50 cm³/10min |
density | ISO 1183 | 1.47 g/cm³ | |
melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 2.0to4.5 g/10min |
Thermal performance | Test Condition | Test Method | FKuR Kunststoff GmbH/F 1137 |
---|---|---|---|
melting temperature | ISO 3146 | >155 °C |