PUR-Ether/MDI 110-35 IMR (15% Glass) Covestro - Polycarbonates
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Covestro - Polycarbonates/ 110-35 IMR (15% Glass) |
|---|---|---|---|
| Impact strength of cantilever beam gap | 3.18mm | ASTM D256 | 160 J/m |
| Supplementary Information | Test Condition | Test Method | Covestro - Polycarbonates/ 110-35 IMR (15% Glass) |
|---|---|---|---|
| HeatSag | 121°C,3.18mm | ASTM D3769 | 4.06 mm |
| Mechanical properties | Test Condition | Test Method | Covestro - Polycarbonates/ 110-35 IMR (15% Glass) |
|---|---|---|---|
| Flexural modulus | 65°C,3.18mm | ASTM D790 | 689 MPa |
| elongation | 断裂,3.18mm | ASTM D638 | 75 % |
| Flexural modulus | -30°C,3.18mm | ASTM D790 | 1900 MPa |
| 23°C,3.18mm | ASTM D790 | 1030 MPa | |
| tensile strength | 断裂,3.18mm | ASTM D638 | 22.1 MPa |
| thermosetting | Test Condition | Test Method | Covestro - Polycarbonates/ 110-35 IMR (15% Glass) |
|---|---|---|---|
| Thermosetting components | 按重量计算的混合比 | 100 | |
| 脱模时间 | 0.50 min | ||
| 部件A | 按重量计算的混合比:53 |
| physical property | Test Condition | Test Method | Covestro - Polycarbonates/ 110-35 IMR (15% Glass) |
|---|---|---|---|
| density | ASTMD792 | 1.14 g/cm³ | |
| Shrinkage rate | MD：3.18mm | 内部方法 | 0.70 % |
| elastomer | Test Condition | Test Method | Covestro - Polycarbonates/ 110-35 IMR (15% Glass) |
|---|---|---|---|
| elongation | 断裂,3.18mm | ASTM D412 | 75 % |
| tear strength | 3.18mm | ASTM D624 | 105 kN/m |
| tensile strength | 断裂,3.18mm | ASTM D412 | 22.1 MPa |
| Thermal performance | Test Condition | Test Method | Covestro - Polycarbonates/ 110-35 IMR (15% Glass) |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：3.18mm | ASTM D696 | 5E-05 cm/cm/°C |