PBT/PC V3900WX-1001 SABIC INNOVATIVE SHANGHAI
VALOX™
Automotive sector、Charging station、Electronic and electrical、Lighting applications、Communication equipment、Wire and cable
High impact、Low warpage、Dimensional stability、High toughness、Weather resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/V3900WX-1001 |
|---|---|---|---|
| Izod Notched -30 ℃ (-22 ℉) | 80*10*4 | ISO 180/1A | 8 kJ/m² |
| ASTM D3763 | 50 J | ||
| Izod Notched at 23 ℃ (73 ℉) | ASTM D256 | 800 J/m | |
| 80*10*4 | ISO 180/1A | 45 kJ/m² | |
| Charpy Notched at 23 ℃ (73 ℉) | V-notch | ISO 179/1eA | 52 kJ/m² |
| Izod Notched -30 ℃ (-22 ℉) | ASTM D256 | 110 J/m |
| Electrical Property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/V3900WX-1001 |
|---|---|---|---|
| UV exposure, water exposure test, and immersion | UL 746C | F1 | |
| Burning wire flammability index (GWFI) 3mm | IEC 60695-2-12 | 960 passes | |
| Heating wire ignition temperature (GWIT) 1.0mm | IEC 60695-2-13 | 825 | |
| Heating wire ignition temperature (GWIT) 3.0mm | IEC 60695-2-13 | 725 by VDE |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/V3900WX-1001 |
|---|---|---|---|
| Tensile strength fracture (brk) | Type I, 50 | ASTM D638 | 43 Mpa |
| Flexural modulus | 1.3 mm/m | ASTM D790 | 2200 Mpa |
| 50 mm/m | ISO 527 | 42 | |
| Tensile strength yield (yld) | Internal | 48 Mpa | |
| Type I, 50 | ASTM D638 | 53 Mpa | |
| Tensile strength fracture (brk) | 50 mm/m | ISO 527 | 40 Mpa |
| ASTM D638 | 250 | ||
| Flexural modulus | 2 mm/m | ISO 178 | 2130 Mpa |
| Type I, 50 | ASTM D638 | 50 | |
| Tensile modulus | 5 mm/mi | ASTM D638 | 2200 Mpa |
| 2 mm/m | ISO 178 | 73 Mpa | |
| Tensile modulus | 1 mm/mi | ISO 527 | 2090 Mpa |
| Tensile strength yield (yld) | 50 mm/m | ISO 527 | 51 Mpa |
| 1.3 mm | ASTM D790 | 80 Mpa |
| combustibility | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/V3900WX-1001 |
|---|---|---|---|
| UL fire rating 5VA | UL94 | 3 mm | |
| UL fire rating V-0 | UL94 | 1.5 mm | |
| Burning wire flammability index (GWFI) 1mm | IEC 60695-2-12 | 960 passes at |
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/V3900WX-1001 |
|---|---|---|---|
| Vicat softening temperature | Rate B/50 | ASTM D1525 | 105 °C |
| Coefficient of Linear Expansion (CLTE) Across Flow | -40°C to 4 | ASTM E831 | 89.7 E-6 °C |
| Relative Temperature Index (RTI) intensity w/o impact- | UL 746B | 120 °C | |
| Coefficient of Linear Expansion (CLTE) Longitudinal (Flow) | -40°C to 4 | ISO 11359-2 | 88.4 E-6 °C |
| Vicat softening temperature | Rate B/5 | ISO 306 | 121 °C |
| Relative Temperature Index (RTI) impact w/impact- | UL 746B | 120 °C | |
| Ball indentation temperature | Pass | IEC 60695-10-2 | 125 °C |
| Relative Temperature Index (RTI) Electrical Elec- | UL 746B | 120 °C | |
| Coefficient of Linear Expansion (CLTE) Longitudinal (Flow) | -40°C to 4 | ASTM E831 | 88.4 E-6 °C |
| Coefficient of Linear Expansion (CLTE) Across Flow | -40°C to 4 | ISO 11359-2 | 89.7 E-6 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/V3900WX-1001 |
|---|---|---|---|
| Water absorption rate | 23°C/sat | ISO 62 | 0.1 |
| Moisture absorption rate | 23°C / 50 | ISO 62 | 0.03 |
| Melt Volume Flow Rate (MVR) 265 ° C/2.16 kg | ISO 1133 | 11 cm³/10 min | |
| Longitudinal shrinkage rate (Flow) | flow, 3.2 | Internal | 0.7~1 |
| Melt Mass Flow Rate (MFR) 266 ° C/5kg | ASTM D1238 | 35 g/10min |