PC GSH2030R2 MITSUBISHI ENGINEERING JAPAN
IUPILON™ 
Automotive Applications,electrical equipment
Glass fiber reinforced,Filler: Glass fiber reinf,30% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/GSH2030R2
Impact strength of simply supported beam without notch23°CISO 17950 kJ/m²
Mechanical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/GSH2030R2
Tensile modulusISO 527-28900 Mpa
bending strengthISO 178180 Mpa
Tensile strain断裂ISO 527-22.5 %
Flexural modulusISO 1788500 Mpa
tensile strength 断裂ISO 527-2120 Mpa
Electrical performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/GSH2030R2
dielectric strength1.00mmIEC 60243-132 KV/mm
Volume resistivityIEC 600932E+16 ohms·cm
relative permittivity100HzIEC 602503.60
Dissipation Factor100HzIEC 602501.1E-03
dielectric strength3.00mmIEC 60243-120 KV/mm
relative permittivity1MHzIEC 602503.50
Surface ResistivityIEC 600932E+15 ohms
Compared to the Leakage Tracking Index (CTI)CTIUL 746PLC 4
Dissipation Factor1MHzIEC 602508.4E-03
flammabilityTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/GSH2030R2
UL flame retardant rating0.40mmUL 94HB
physical property Test ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/GSH2030R2
Shrinkage rateTD:3.20mm0.25-0.45 %
吸水率(饱和,23°C)0.090 %
Melt volume flow rate300°C/1.2kgISO 11334.80 cm3/10min
Shrinkage rateMD:3.20mm0.050-0.25 %
melt mass-flow rate300°C/1.2kgISO 11335.7 g/10min
Thermal performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/GSH2030R2
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B148 °C
1.8MPa,未退火，HDTISO 75-2/A144 °C
Linear coefficient of thermal expansionMDISO 11359-21.8E-05 cm/cm/°C
TDISO 11359-26.3E-05 cm/cm/°C