PC Iupilon® RS-3001R Mitsubishi Chemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupilon® RS-3001R |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 63 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| Mechanical properties | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupilon® RS-3001R |
|---|---|---|---|
| Nominal tensile fracture strain | ISO 527-2 | 120 % | |
| Tensile modulus | ISO 527-2 | 2500 MPa | |
| Tensile strain | 屈服 | ISO 527-2 | 6.7 % |
| tensile strength | 屈服 | ISO 527-2 | 62.0 MPa |
| Flexural modulus | ISO 178 | 2100 MPa | |
| bending strength | ISO 178 | 90.0 MPa |
| Electrical performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupilon® RS-3001R |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 3E+16 ohms·cm | |
| Surface Resistivity | IEC 60093 | 6E+15 ohms |
| physical property | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupilon® RS-3001R |
|---|---|---|---|
| Shrinkage rate | TD:3.20mm | 0.50to0.70 % | |
| MD:3.20mm | 0.50to0.70 % | ||
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 15.0 cm³/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.24 % |
| density | ISO 1183 | 1.21 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 15 g/10min |
| Thermal performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupilon® RS-3001R |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 139 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 126 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| TD | ISO 11359-2 | 6.6E-05 cm/cm/°C |