PPO(PPE) Iupiace® EHM1010A Mitsubishi Chemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupiace® EHM1010A |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 3.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 20 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupiace® EHM1010A |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 3800 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.2 % |
| Tensile modulus | 23°C | ISO 527-2 | 3700 MPa |
| tensile strength | 断裂,23°C | ISO 527-2 | 64.0 MPa |
| bending strength | 23°C | ISO 178 | 101 MPa |
| Electrical performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupiace® EHM1010A |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 6E+05 ohms |
| physical property | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupiace® EHM1010A |
|---|---|---|---|
| Shrinkage rate | TD:3.20mm | 0.55to0.75 % | |
| MD:3.20mm | 0.55to0.75 % | ||
| density | ISO 1183 | 1.16 g/cm³ |
| Thermal performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupiace® EHM1010A |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 165 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 155 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 5.3E-05 cm/cm/°C |
| TD | ISO 11359-2 | 5.5E-05 cm/cm/°C |