Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EM9417 703181 COVESTRO SHANGHAI
Makrolon®
Automotive Applications、Casters
High impact resistance、Flame retardant、Filler: Glass fiber reinf、10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | COVESTRO SHANGHAI/EM9417 703181 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C,CompleteBreak | ISO 179/1eU | 75 kJ/m² |
| Mechanical properties | Test Condition | Test Method | COVESTRO SHANGHAI/EM9417 703181 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 15 % |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 45.0 Mpa |
| Tensile modulus | 23°C | ISO 527-2/1 | 3700 Mpa |
| Tensile strain | 屈服,23°C | ISO 527-2/5 | 5.0 % |
| tensile strength | 屈服,23°C | ISO 527-2/5 | 60.0 Mpa |
| Electrical performance | Test Condition | Test Method | COVESTRO SHANGHAI/EM9417 703181 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | V |
| Volume resistivity | 23°C | IEC 60093 | 1E+16 ohms·cm |
| Surface Resistivity | IEC 60093 | 1E+16 ohms |
| flammability | Test Condition | Test Method | COVESTRO SHANGHAI/EM9417 703181 |
|---|---|---|---|
| Burning wire flammability index | 1.6mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Limiting Oxygen Index | ISO 4589-2 | 35 % |
| physical property | Test Condition | Test Method | COVESTRO SHANGHAI/EM9417 703181 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 2577 | 0.40-0.60 % |
| TD:2.00mm2 | ISO 294-4 | 0.50 % | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 6.00 cm3/10min |
| Shrinkage rate | MD | ISO 2577 | 0.40-0.60 % |
| MD:2.00mm2 | ISO 294-4 | 0.60 % |
| Thermal performance | Test Condition | Test Method | COVESTRO SHANGHAI/EM9417 703181 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 144 °C |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 4E-05 cm/cm/°C |
| RTI Imp | 1.5mm | UL 746 | 115 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 141 °C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 6E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 135 °C |
| vicat | -- | ISO 306/B50 | 143 °C |
| RTI Str | 1.5mm | UL 746 | 125 °C |
| RTI Elec | 1.5mm | UL 746 | 125 °C |