Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
MMS DENKA Transparent Polymer TX-100S 日本电气化学
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 日本电气化学/DENKA Transparent Polymer TX-100S |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 2.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | 日本电气化学/DENKA Transparent Polymer TX-100S |
|---|---|---|---|
| Nominal tensile fracture strain | ISO 527-2/5 | 6.0 % | |
| tensile strength | 断裂 | ISO 527-2/5 | 67.0 MPa |
| Flexural modulus | ISO 178 | 3400 MPa | |
| bending strength | ISO 178 | 115 MPa |
| optical performance | Test Condition | Test Method | 日本电气化学/DENKA Transparent Polymer TX-100S |
|---|---|---|---|
| transmissivity | 2000µm | ISO 13468-1 | 92.0 % |
| refractive index | ASTM D542 | 1.540 | |
| Haze ratio | 2000µm | ISO 14782 | 0.20 % |
| flammability | Test Condition | Test Method | 日本电气化学/DENKA Transparent Polymer TX-100S |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | 日本电气化学/DENKA Transparent Polymer TX-100S |
|---|---|---|---|
| Shrinkage rate | 2.00mm | 内部方法 | 0.40 % |
| density | 23°C | ISO 1183 | 1.13 g/cm³ |
| melt mass-flow rate | 200°C/5.0kg | ISO 1133 | 1.8 g/10min |
| Water absorption rate | 平衡 | ASTM D570 | 0.12 % |
| Thermal performance | Test Condition | Test Method | 日本电气化学/DENKA Transparent Polymer TX-100S |
|---|---|---|---|
| vicat | ISO 306/B | 100 °C | |
| Hot deformation temperature (HDT) | 1.8MPa,未退火，HDT | ISO 75-2/Af | 79.0 °C |