PC HF1130-111 SABIC INNOVATIVE CHONGQING
LEXAN™
Automotive sector
heat-resisting、Dimensional stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/HF1130-111 |
|---|---|---|---|
| Tensile impact strength 4 | ASTMD1822 | 378 kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,EnergyatPeakLoad | ASTMD3763 | 54.2 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/HF1130-111 |
|---|---|---|---|
| elongation | 断裂 | ASTMD638 | 110 % |
| tensile strength | 屈服 | ASTMD638 | 62.1 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTMD790 | 93.1 Mpa |
| tensile strength | 断裂 | ASTMD638 | 65.5 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTMD790 | 2310 Mpa |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/HF1130-111 |
|---|---|---|---|
| transmissivity | 2540µm | ASTMD1003 | 88.0 % |
| Haze ratio | 2540µm | ASTMD1003 | 1.0 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/HF1130-111 |
|---|---|---|---|
| FlameRating | 1.2mm | UL94 | V-2 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/HF1130-111 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| melt mass-flow rate | 300°C/1.2kg | ASTMD1238 | 25 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/HF1130-111 |
|---|---|---|---|
| RTI Str | UL746 | 130 °C | |
| RTI Elec | UL746 | 130 °C | |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 127 °C |
| RTI Imp | UL746 | 130 °C |