Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PTFE M111(微粉) DAIKIN JAPAN
POLYFLON™
--
--
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | DAIKIN JAPAN/M111(微粉) |
|---|---|---|---|
| StretchingVoidIndex | ASTM D4895 | 62.0 | |
| MITFlexuralLife | ASTM D2178 | 3E+06 |
| Mechanical properties | Test Condition | Test Method | DAIKIN JAPAN/M111(微粉) |
|---|---|---|---|
| Heat distortion temperature | 200°C,6.9MPa，HDT | ASTM D621 | 14.9 % |
| elongation | 断裂,1.50mm | ASTM D4894 | 500 % |
| Heat distortion temperature | 25°C,14MPa，HDT | ASTM D621 | 10.6 % |
| tensile strength | 屈服,1.50mm | ASTM D4894 | 40.0 Mpa |
| compressive strength | 0%应变2 | ASTM D695 | 8.70 Mpa |
| 25%应变3 | ASTM D695 | 28.6 Mpa | |
| Heat distortion temperature | 100°C,14MPa，HDT | ASTM D621 | 21.7 % |
| compressive strength | 1%应变3 | ASTM D695 | 5.90 Mpa |
| Electrical performance | Test Condition | Test Method | DAIKIN JAPAN/M111(微粉) |
|---|---|---|---|
| Dissipation Factor | 1kHz | ASTM D150 | <1.0E-4 |
| Volume resistivity | ASTM D257 | >1.0E+18 ohms·cm | |
| Surface Resistivity | ASTM D257 | >1.0E+15 ohms | |
| dielectric strength | 140 KV/mm | ||
| dielectric constant | 1kHz | ASTM D150 | <2.10 |
| physical property | Test Condition | Test Method | DAIKIN JAPAN/M111(微粉) |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 4.4 % |
| Apparent density | ASTM D4894 | 0.36 g/cm³ |
| elastomer | Test Condition | Test Method | DAIKIN JAPAN/M111(微粉) |
|---|---|---|---|
| compression set | 100°C4 | ASTM D621 | 7.4 % |
| 25°C4 | ASTM D621 | 3.0 % | |
| 200°C5 | ASTM D621 | 4.1 % |
| Thermal performance | Test Condition | Test Method | DAIKIN JAPAN/M111(微粉) |
|---|---|---|---|
| melting temperature | DSC | 324 °C | |
| Continuous use temperature | 260 °C |