Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS Sindustris ABS LXR501 Sincerity Australia Pty Ltd.
--
Automotive internal parts and casing
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Sincerity Australia Pty Ltd./Sindustris ABS LXR501 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 120 J/m |
| 23°C,6.40mm | ASTM D256 | 110 J/m | |
| -30°C,6.40mm | ASTM D256 | 59 J/m | |
| -30°C,3.20mm | ASTM D256 | 59 J/m |
| hardness | Test Condition | Test Method | Sincerity Australia Pty Ltd./Sindustris ABS LXR501 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 114 |
| Mechanical properties | Test Condition | Test Method | Sincerity Australia Pty Ltd./Sindustris ABS LXR501 |
|---|---|---|---|
| elongation | 断裂,3.20mm | ASTM D638 | 15 % |
| bending strength | 3.20mm | ASTM D790 | 76.5 MPa |
| elongation | 屈服,3.20mm | ASTM D638 | >5.0 % |
| Flexural modulus | 3.20mm | ASTM D790 | 2650 MPa |
| tensile strength | 屈服,3.20mm | ASTM D638 | 47.1 MPa |
| flammability | Test Condition | Test Method | Sincerity Australia Pty Ltd./Sindustris ABS LXR501 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | Sincerity Australia Pty Ltd./Sindustris ABS LXR501 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.40to0.70 % |
| density | ASTM D792 | 1.07 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 3.0 g/10min |
| Thermal performance | Test Condition | Test Method | Sincerity Australia Pty Ltd./Sindustris ABS LXR501 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 113 °C |
| vicat | ASTM D15254 | 111 °C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 104 °C |