Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC D551-7M10203 SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Outdoor applications、Electronic and Electrical、Plastic bag、Architectural Application
Glass fiber reinforced、Non chloro non bromine fl
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/D551-7M10203 |
|---|---|---|---|
| Linear thermal expansion coefficient | MD:-40到40°C | ASTME831 | 1.4E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 107 °C |
| Linear thermal expansion coefficient | TD:-40到40°C | ASTME831 | 5.1E-05 cm/cm/°C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/D551-7M10203 |
|---|---|---|---|
| Melt Mass-Flow Rate | 300°C/2.16kg | ASTMD1238 | 13 g/10min |
| 300°C/5.0kg | ASTMD1238 | 49 g/10min | |
| Modeling Shrinkage | TD:24小时 | ASTMD955 | 0.050到0.20 % |
| MD:24小时 | ASTMD955 | 0.050到0.20 % | |
| Melt Volume flow Rate | 300°C/5.0kg | ASTMD1238 | 29.5 cm3/10min |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/D551-7M10203 |
|---|---|---|---|
| ASTMD638 | 15300 Mpa | ||
| Break | ASTMD638 | 154 Mpa | |
| fracture | ISO527-2/5 | 153 Mpa | |
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 14900 Mpa |
| Break | ASTMD638 | 2.1 % | |
| fracture | ISO527-2/5 | 1.9 % | |
| Flexural Strength | 断裂,50.0mm跨距 | ASTMD790 | 223 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/D551-7M10203 |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 38 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 12 kJ/m² |
| Unnotched Izod Impact Strength | 23°C | ASTMD4812 | 520 J/m |
| Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 21.0 J |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/D551-7M10203 |
|---|---|---|---|
| Flame Rating | 1.00mm | UL94 | V-0 |