Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM Z2320-003 BASF GERMANY
Ultraform®
Toy、Automotive Applications、Thin walled components
High toughness
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/Z2320-003 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.5 kJ/m² |
| -30°C | ISO 179/1eA | 4.5 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 130 kJ/m² |
| -30°C | ISO 179/1eU | 130 kJ/m² |
| hardness | Test Condition | Test Method | BASF GERMANY/Z2320-003 |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 150 Mpa |
| Supplementary Information | Test Condition | Test Method | BASF GERMANY/Z2320-003 |
|---|---|---|---|
| ISOType | ISO 9988-1 | POM-K.M-GNR.06-002 |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/Z2320-003 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2800 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 65.0 Mpa |
| Tensile creep modulus | 1000hr | ISO 899-1 | 1350 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 7.0 % |
| Nominal tensile fracture strain | ISO 527-2/50 | 20 % |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/Z2320-003 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | V |
| relative permittivity | 1MHz | IEC 60250 | 3.80 |
| Surface Resistivity | IEC 60093 | 1E+13 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 5E-03 |
| flammability | Test Condition | Test Method | BASF GERMANY/Z2320-003 |
|---|---|---|---|
| Flammability level | 1.6mm | IEC 60695-11-10,-20 | HB |
| physical property | Test Condition | Test Method | BASF GERMANY/Z2320-003 |
|---|---|---|---|
| Apparent density | 0.85 g/cm³ | ||
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 42.0 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 2.1 % |
| MD | ISO 294-4 | 2.0 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| 饱和,23°C | ISO 62 | 0.80 % | |
| density | ISO 1183 | 1.40 g/cm³ |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/Z2320-003 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 166 °C | |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 105 °C |
| maximum service temperature | 短周期操作 | 100 °C |