COC 6015S-04 TOPAS GERMANY
TOPAS®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
thermal performance | Test Condition | Test Method | TOPAS GERMANY/6015S-04 |
---|---|---|---|
Glass transition temperature | 10℃/min | ISO 11357 | 158 °C |
Hot deformation temperature | 0.45MPa | ISO 75 | 150 °C |
Vicat softening temperature | 50℃/hr 50N | ISO 306 | 156 °C |
mechanical properties | Test Condition | Test Method | TOPAS GERMANY/6015S-04 |
---|---|---|---|
Charpy Notched Impact Strength | 23℃ | ISO 179 | 15 kJ/㎡ |
23℃1eA型 | ISO 179 | 1.6 kJ/㎡ | |
elongation | Break5mm/min | ISO 527 | 2.5 % |
Tensile modulus | 1.0mm/min | ISO 527 | 3000 ㎫ |
tensile strength | Break5mm/min | ISO 527 | 60 ㎫ |
flame retardant performance | Test Condition | Test Method | TOPAS GERMANY/6015S-04 |
---|---|---|---|
UL flame retardant rating | 1.5mm | UL 94 | HB |
Electrical performance | Test Condition | Test Method | TOPAS GERMANY/6015S-04 |
---|---|---|---|
Dielectric constant | 1GHz | IEC 60250 | 2.3 |
1kHz-10kHz | IEC 60250 | 2.35 | |
Dissipation factor | 1GHz | IEC 60250 | 0.000070 |
Volume resistivity | IEC 60093 | 100000000000000 Ω.m |
Physical properties | Test Condition | Test Method | TOPAS GERMANY/6015S-04 |
---|---|---|---|
density | ISO 1183 | 1020 kg/㎤ | |
melt mass-flow rate | 260℃ 2.16kg | ISO 1133 | 4 ㎤/10min |
Water absorption rate | 23℃Saturation | ISO 62 | 0.01 % |
UL | Test Condition | Test Method | TOPAS GERMANY/6015S-04 |
---|---|---|---|
RTI Elec | 全色 1.5mm | UL 746B | 100 °C |
RTI Imp | 全色 1.5mm | UL 746B | 50 °C |
RTI Str | 全色 1.5mm | UL 746B | 50 °C |
UL flame retardant rating | 1.5mm | UL 94 | HB |
optical performance | Test Condition | Test Method | TOPAS GERMANY/6015S-04 |
---|---|---|---|
Refractive index | 25℃ 589nm | ISO 489 | 1.53 |
transmissivity | ISO 13468 | 91 % |