Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
SPS N WA 7030 IDEMITSU JAPAN
XAREC™
Electrical applications、Household daily necessiti
Glass fiber reinforced、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | IDEMITSU JAPAN/N WA 7030 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 57 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 68 kJ/m² |
| Electrical performance | Test Condition | Test Method | IDEMITSU JAPAN/N WA 7030 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 6.7E+15 ohms·cm | |
| Hot wire ignition (HWI) | 1.5mm | UL 746 | PLC 4 |
| dielectric strength | ASTM D149 | 18 KV/mm | |
| dielectric constant | 1MHz | IEC 60250 | 3.20 |
| Compared to the Leakage Tracking Index (CTI) | CTI)3 | IEC 60112 | PLC 2 |
| High arc combustion index (HAI) | 1.5mm | UL 746 | PLC 0 |
| arc resistance | ASTM D495 | PLC 5 | |
| Hot wire ignition (HWI) | 3.0mm | UL 746 | PLC 4 |
| High arc combustion index (HAI) | 3.0mm | UL 746 | PLC 0 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.069 |
| Mechanical properties | Test Condition | Test Method | IDEMITSU JAPAN/N WA 7030 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 10000 Mpa | |
| bending strength | ISO 178 | 250 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.6 % |
| Flexural modulus | ISO 178 | 9100 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 175 Mpa |
| flammability | Test Condition | Test Method | IDEMITSU JAPAN/N WA 7030 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | IDEMITSU JAPAN/N WA 7030 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.20-0.50 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| Shrinkage rate | TD | 内部方法 | 0.60-0.90 % |
| Thermal performance | Test Condition | Test Method | IDEMITSU JAPAN/N WA 7030 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-30to30°C | TMA | 4.9E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 260 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 245 °C | |
| Linear coefficient of thermal expansion | MD：-30到30°C | TMA | 2.4E-05 cm/cm/°C |
| RTI Imp | UL 746 | 50.0 °C | |
| RTI Str | UL 746 | 50.0 °C | |
| RTI Elec | UL 746 | 50.0 °C |