Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 209AW JAPAN POLYPLASTIC
DURANEX® 
Fitness equipment,Casters
Low friction coefficient,wear resistant,Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodJAPAN POLYPLASTIC/209AW
Rockwell hardnessM-ScaleISO 2039-275
Supplementary InformationTest ConditionTest MethodJAPAN POLYPLASTIC/209AW
ColourNumberEF2001
thermal performanceTest ConditionTest MethodJAPAN POLYPLASTIC/209AW
Combustibility (rate)UL 94V-0
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A73.0 °C
1.8MpaISO 75-1/-273 °C
Linear coefficient of thermal expansionMD：23to55°CInternal Method1E-04 cm/cm/°C
ASTM D696/ISO 11359- mm/mm.℃
TD：23to55°CInternal Method1E-04 cm/cm/°C
UL flame retardant ratingUL 94V-0
mechanical propertiesTest ConditionTest MethodJAPAN POLYPLASTIC/209AW
Bending modulusISO 1782780 Mpa
ASTM D790/ISO 1782780 kg/cm²(MPa)[Lb/in²]
bending strengthASTM D790/ISO 17882 kg/cm²(MPa)[Lb/in²]
ISO 17882 Mpa
Charpy Notched Impact StrengthISO 179/1eA3.5 kJ/m²
Elongation at BreakASTM D638/ISO 5275 %
Tensile strainBreakISO 527-25.0 %
tensile strengthISO 527-1/-252 Mpa
ASTM D638/ISO 52752 kg/cm²(MPa)[Lb/in²]
ISO 527-252.0 Mpa
Electrical performanceTest ConditionTest MethodJAPAN POLYPLASTIC/209AW
Dielectric strength3.00mmIEC 60243-118 KV/mm
Volume resistivityIEC 600934E+16 ohms·cm
ASTM D257/IEC 60093- Ω.cm
Physical propertiesTest ConditionTest MethodJAPAN POLYPLASTIC/209AW
densityASTM D792/ISO 11831.45
Water absorption rate23°C,24hrISO 620.20 %
flammabilityTest ConditionTest MethodJAPAN POLYPLASTIC/209AW
UL flame retardant ratingUL 94V-0