Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO SE1GFN1-701 SABIC INNOVATIVE US
NORYL™
Electronic communication 、Electronic communication 、Household appliances、Household appliances、Automotive interior parts、Sports Equipment、Above water
enhance、Glass fiber reinforced、Flame retardant、High mobility、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/SE1GFN1-701 |
|---|---|---|---|
| Rockwell hardness | L 计秤 | ASTM D785 | 104 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/SE1GFN1-701 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 5.0 % |
| bending strength | 断裂, 50.0 mm 跨距 | ASTM D790 | 119 Mpa |
| tensile strength | 断裂 | ASTM D638 | 74.0 Mpa |
| Flexural modulus | 50.0 mm 跨距 | ASTM D790 | 3990 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/SE1GFN1-701 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1.0E+15 ohms·cm | |
| dielectric constant | 60 Hz | ASTM D150 | 3.00 |
| Dissipation Factor | 60 Hz | ASTM D150 | 1.7E-3 |
| 50 Hz | ASTM D150 | 1.7E-3 | |
| dielectric constant | 1 MHz | ASTM D150 | 3.00 |
| Hot wire ignition (HWI) | UL 746 | PLC 1 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | |
| Dissipation Factor | 1 MHz | ASTM D150 | 1.6E-3 |
| High arc combustion index (HAI) | UL 746 | PLC 2 | |
| dielectric constant | 50 kHz | ASTM D150 | 3.00 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/SE1GFN1-701 |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | V-1 |
| Limiting Oxygen Index | ASTM D2863 | 34 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/SE1GFN1-701 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C | ASTM D570 | 0.22 % |
| 24 hr | ASTM D570 | 0.070 % | |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.30 - 0.50 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/SE1GFN1-701 |
|---|---|---|---|
| vicat | ASTM D15254 | 147 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 131 °C |
| RTI Imp | UL 746 | 105 °C | |
| RTI | UL 746 | 110 °C | |
| RTI Elec | UL 746 | 110 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/SE1GFN1-701 |
|---|---|---|---|
| drying time | 3.0 to 4.0 hr | ||
| screw speed | 20 to 100 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 260 to 305 °C | ||
| Temperature at the rear of the barrel | 250 to 300 °C | ||
| Processing (melt) temperature | 280 to 310 °C | ||
| drying temperature | 105 to 110 °C | ||
| Suggested injection volume | 30 to 70 % | ||
| Temperature at the front of the material cylinder | 270 to 310 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 75 to 105 °C | ||
| Spray nozzle temperature | 280 to 310 °C |