Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 DPAKV30FN00 ENVALIOR WUXI
Durethan®
--
Filler: Glass fiber reinf、30%、Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ENVALIOR WUXI/DPAKV30FN00 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 90 kJ/m² |
| -30°C | ISO179/1eU | 70 kJ/m² |
| hardness | Test Condition | Test Method | ENVALIOR WUXI/DPAKV30FN00 |
|---|---|---|---|
| ISO2039-1 | 230 Mpa |
| Supplementary Information | Test Condition | Test Method | ENVALIOR WUXI/DPAKV30FN00 |
|---|---|---|---|
| ISO Shortcut | ISO1874 | PA66,GR,14-110,GF30 |
| Electrical performance | Test Condition | Test Method | ENVALIOR WUXI/DPAKV30FN00 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | 1E+14 ohms | |
| Volume resistivity | 23°C | IEC60093 | 1E+15 ohms·cm |
| 23°C,100Hz | IEC60250 | 4.00 | |
| 23°C,1MHz | IEC60250 | 4.00 | |
| CTI | 解决方案A | IEC60112 | 600 V |
| dielectric strength | 23°C,1.00mm | IEC60243-1 | 40 KV/mm |
| Dissipation Factor | 23°C,100Hz | IEC60250 | 9E-03 |
| 23°C,1MHz | IEC60250 | 0.018 |
| Mechanical properties | Test Condition | Test Method | ENVALIOR WUXI/DPAKV30FN00 |
|---|---|---|---|
| Flexural modulus | 23°C | ISO178/A | 8400 Mpa |
| 23°C | ASTMD790 | 841 Mpa | |
| Bending stress | 23°C | ISO178 | 290 Mpa |
| Tensile modulus | 23°C | ASTMD638 | 10300 Mpa |
| Bending stress | 3.5%Strain | ISO178/A | -- Mpa |
| Tensile strain | 断裂,23°C | ISO527-2/5 | 3.0 % |
| elongation | 断裂,23°C | ASTMD638 | 3.0 % |
| Tensile stress | 断裂,23°C | ISO527-2/5 | 185 Mpa |
| tensile strength | 断裂,23°C | ASTMD638 | 179 Mpa |
| Tensile modulus | 23°C | ISO527-2/1 | 10600 Mpa |
| bending strength | 23°C | ASTMD790 | 290 Mpa |
| Bending stress | FlexuralStrainatFlexuralStrength5(23°C) | 4.0 % |
| flammability | Test Condition | Test Method | ENVALIOR WUXI/DPAKV30FN00 |
|---|---|---|---|
| Burning wire flammability index | 2.0mm | IEC60695-2-12 | 600 °C |
| UL flame retardant rating | 3.2mm | UL94 | HB |
| Extreme Oxygen Index 7 | ISO4589-2 | 23 % | |
| UL flame retardant rating | 1.6mm | UL94 | HB |
| physical property | Test Condition | Test Method | ENVALIOR WUXI/DPAKV30FN00 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 2.0 % |
| 饱和,23°C | ISO62 | 5.5 % | |
| Shrinkage rate | MD:120°C,2hr,3.00mm3 | ISO2577 | 0.040 % |
| TD:280°C,3.00mm2 | ISO2577 | 1.5 % | |
| Apparent density | ISO60 | 0.70 g/cm³ | |
| Shrinkage rate | MD:280°C,3.00mm2 | ISO2577 | 0.35 % |
| TD:120°C,2hr,3.00mm3 | ISO294-4 | 0.050 % |
| Thermal performance | Test Condition | Test Method | ENVALIOR WUXI/DPAKV30FN00 |
|---|---|---|---|
| 0.45MPa,未退火 | ISO75-2/B | 250 °C | |
| 1.8MPa,未退火 | ISO75-2/A | 250 °C | |
| 8.0MPa,未退火 | ISO75-2/C | 135 °C | |
| Melting temperature 5 | ISO11357-3 | 263 °C | |
| vicat | ISO306/B120 | >230 °C | |
| TD：23to55°C | ISO11359-2 | 1E-04 cm/cm/°C | |
| MD：23到55°C | ISO11359-2 | 2.5E-05 cm/cm/°C |