PEEK 90GL30 VICTREX UK
VICTREX®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | VICTREX UK/90GL30 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 45 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1U | 45 kJ/m² |
| hardness | Test Condition | Test Method | VICTREX UK/90GL30 |
|---|---|---|---|
| Shore hardness | 邵氏D,23°C | ISO 868 | 87 |
| Mechanical properties | Test Condition | Test Method | VICTREX UK/90GL30 |
|---|---|---|---|
| bending strength | 275°C | ISO 178 | 75.0 Mpa |
| tensile strength | 断裂,275°C | ISO 527-2 | 45.0 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 12000 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 195 Mpa |
| compression stress | 23°C | ISO 604 | 250 Mpa |
| tensile strength | 断裂,175°C | ISO 527-2 | 80.0 Mpa |
| bending strength | 175°C | ISO 178 | 115 Mpa |
| tensile strength | 断裂,125°C | ISO 527-2 | 130 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.4 % |
| bending strength | 23°C | ISO 178 | 290 Mpa |
| compression stress | 120°C | ISO 604 | 160 Mpa |
| bending strength | 125°C | ISO 178 | 230 Mpa |
| Flexural modulus | 23°C | ISO 178 | 11500 Mpa |
| compression stress | 250°C | ISO 604 | 55.0 Mpa |
| tensile strength | 断裂,225°C | ISO 527-2 | 60.0 Mpa |
| Electrical performance | Test Condition | Test Method | VICTREX UK/90GL30 |
|---|---|---|---|
| dielectric constant | 23°C,1kHz | IEC 60250 | 3.30 |
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| dielectric strength | 2.00mm | IEC 60243-1 | 23 KV/mm |
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 4E-03 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| flammability | Test Condition | Test Method | VICTREX UK/90GL30 |
|---|---|---|---|
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 960 °C |
| Filling analysis | Test Condition | Test Method | VICTREX UK/90GL30 |
|---|---|---|---|
| melt viscosity | 400°C | ISO 11443 | 200 Pa·s |
| physical property | Test Condition | Test Method | VICTREX UK/90GL30 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.90 % |
| spiral flow length | --5 | 内部方法 | 18.5 CM |
| Shrinkage rate | MD | ISO 294-4 | 0.30 % |
| spiral flow length | --6 | 内部方法 | 22.0 CM |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.30 % |
| 100°C，饱和 | ISO 62 | 0.450 % |
| Thermal performance | Test Condition | Test Method | VICTREX UK/90GL30 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 335 °C |
| melting temperature | ISO 11357-3 | 343 °C | |
| Linear coefficient of thermal expansion | MD:>143°C | ISO 11359-2 | 2E-05 cm/cm/°C |
| thermal conductivity | 23°C9 | ISO 22007-4 | 0.30 W/m/K |
| Linear coefficient of thermal expansion | MD:<143°C | ISO 11359-2 | 2E-05 cm/cm/°C |
| thermal conductivity | 23°C10 | ISO 22007-4 | 0.35 W/m/K |
| Glass Transition Temperature | ISO 11357 | 143 °C | |
| Linear coefficient of thermal expansion | TD:>143°C | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| TD:<143°C | ISO 11359-2 | 4.5E-05 cm/cm/°C |