ABS PA-727 TAIWAN CHIMEI
POLYLAC® 
Automotive sector,Sanitary Ware,Household goods
High gloss,High toughness,High rigidity
SGSULRoHS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

machinabilityTest ConditionTest MethodTAIWAN CHIMEI/PA-727
Dry conditions于85°C下烘料约3-4小时
Melt Temperature- °C
Mold temperature30-70°C °C
pressure- Mpa
Processing temperature180-230°C °C
Screw speed- rpm
thermal performanceTest ConditionTest MethodTAIWAN CHIMEI/PA-727
Combustibility (rate)UL 941/16“HB
Hot deformation temperatureHDTASTM D648/ISO 7588(190) ℃（℉）
Linear coefficient of thermal expansionASTM D696/ISO 11359- mm/mm.℃
Vicat softening temperatureASTM D1525/ISO R306105(221) ℃（℉）
mechanical propertiesTest ConditionTest MethodTAIWAN CHIMEI/PA-727
Bending modulusASTM D790/ISO 1782700(38000) kg/cm²(MPa)[Lb/in²]
bending strengthASTM D790/ISO 178780(11.000) kg/cm²(MPa)[Lb/in²]
Charpy Notched Impact StrengthASTM D256/ISO 179- kg·cm/cm(J/M)ft·lb/in
elongationASTM D638/ISO 52720 %
Elongation at BreakASTM D638/ISO 527- %
Impact strength of cantilever beam gapASTM D256/ISO 17926(4、8) kg·cm/cm(J/M)ft·lb/in
Rockwell hardnessASTM D785R-110
Tensile modulusASTM D638/ISO 527- kg/cm²(MPa)[Lb/in²]
tensile strengthASTM D638/ISO 527485(6870) kg/cm²(MPa)[Lb/in²]
otherTest ConditionTest MethodTAIWAN CHIMEI/PA-727
characteristic电镀性能佳。
Color-
purpose通用于一切需要电镀装饰配件按纽、音响器材面板、轮胎盖、镜框、时钟外壳和汽车配件等
remarks在射出周期中勿将热融胶长期停留在加热管中
Physical propertiesTest ConditionTest MethodTAIWAN CHIMEI/PA-727
densityASTM D792/ISO 11831.04
melt mass-flow rateASTM D1238/ISO 113319 g/10min
Shrinkage rateASTM D955- %
Water absorption rateASTM D570/ISO 62- %