PA66 1402G BK ASAHI JAPAN
Leona™
Automotive sector,Electronic field,Electrical field,component
High rigidity,high strength,Fatigue resistance,Creep resistance,Thermal stability,Moderate heat resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ASAHI JAPAN/1402G BK |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 72 kJ/m² | |
| Charpy Notched Impact Strength | ISO 179 | 11 kJ/m² | |
| Impact strength of cantilever beam gap | ASTM D256 | 130 J/m |
| hardness | Test Condition | Test Method | ASAHI JAPAN/1402G BK |
|---|---|---|---|
| Rockwell hardness | M 级 | ASTM D785 | 96 |
| M 计秤 | ISO 2039-2 | 96 | |
| R 计秤 | ISO 2039-2 | 120 | |
| R 级 | ASTM D785 | 120 |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/1402G BK |
|---|---|---|---|
| tensile strength | 断裂, 23°C | ISO 527-2 | 190 Mpa |
| Taber abraser | 1000 Cycles | ASTM D1044 | -- mg |
| elongation | 断裂 | ASTM D638 | 3.0 % |
| tensile strength | -- | ASTM D638 | 186 Mpa |
| elongation | 断裂, 23°C | ISO 527-2 | 3.0 % |
| bending strength | -- | ASTM D790 | 289 Mpa |
| 23°C | ISO 178 | 275 Mpa | |
| Flexural modulus | 23°C | ISO 178 | 9000 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 10000 Mpa |
| Flexural modulus | -- | ASTM D790 | 9300 Mpa |
| Electrical performance | Test Condition | Test Method | ASAHI JAPAN/1402G BK |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 3.00 mm | IEC 60112 | V |
| Surface Resistivity | ASTM D257 | 1.0E+15 ohms | |
| Volume resistivity | -- | ASTM D257 | 1.0E+15 ohms·cm |
| 23°C | IEC 60093 | 1.0E+15 ohms·cm | |
| dielectric strength | ASTM D149 | 28 KV/mm |
| flammability | Test Condition | Test Method | ASAHI JAPAN/1402G BK |
|---|---|---|---|
| UL flame retardant rating | 0.75 mm | UL 94 | HB |
| Limiting Oxygen Index | ASTM D2863 | 23 % |
| physical property | Test Condition | Test Method | ASAHI JAPAN/1402G BK |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | -- % |
| Shrinkage rate | 横向流量 | 内部方法 | 0.90 % |
| Water absorption rate | 饱和, 23°C | -- % | |
| Shrinkage rate | 流量 | 内部方法 | 0.40 % |
| density | ASTM D792 | 1.39 g/cm³ |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/1402G BK |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 265 °C |
| thermal conductivity | 0.30 W/m/K | ||
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ASTM D648 | 260 °C |
| 1.8 MPa, 未退火，HDT | ASTM D648 | 250 °C | |
| Linear coefficient of thermal expansion | 流动 | ASTM D696 | 3.0E-5 cm/cm/°C |
| specific heat | 1590 J/kg/°C |