Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP 7705 SABIC INNOVATIVE SHANGHAI
SABIC®
Automotive sector
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/7705 |
|---|---|---|---|
| Suspended wall beam notch impact strength 6 | 0°C | ISO180/1A | 6.0 kJ/m² |
| Dart impact equipped with measuring instruments 9 | 23°C,EnergyatPeakLoad | ASTMD3763 | 22.1 J |
| Suspended wall beam notch impact strength 6 | -30°C | ISO180/1A | 3.0 kJ/m² |
| NotchedIzodImpact8 | 23°C,3.20mm | ASTMD256 | 120 J/m |
| Dart impact equipped with measuring instruments 9 | -30°C,EnergyatPeakLoad | ASTMD3763 | 7.10 J |
| Suspended wall beam notch impact strength 6 | 23°C | ISO180/1A | 20 kJ/m² |
| Dart impact equipped with measuring instruments 9 | 0°C,EnergyatPeakLoad | ASTMD3763 | 19.1 J |
| Cantilever beam without notch impact strength 8 | 23°C,3.20mm | ASTMD4812 | NoBreak |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/7705 |
|---|---|---|---|
| 邵氏D | ISO868 | 60 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/7705 |
|---|---|---|---|
| Tensile stress | 屈服 | ISO527-2/50 | 22.0 Mpa |
| elongation | 屈服 | ASTMD638 | 4.6 % |
| 断裂 | ASTMD638 | 24 % | |
| Tensile modulus | ISO527-2/1 | 2010 Mpa | |
| Flexural modulus | 50.0mm跨距4 | ISO178 | 2080 Mpa |
| tensile strength | 屈服 | ASTMD638 | 23.0 Mpa |
| 断裂 | ASTMD638 | 16.0 Mpa | |
| Tensile strain | 断裂 | ISO527-2/50 | 32 % |
| 屈服 | ISO527-2/50 | 4.4 % | |
| Tensile modulus | ASTMD638 | 1910 Mpa | |
| Flexural modulus | 50.0mm跨距5 | ASTMD790 | 1900 Mpa |
| Tensile stress | 断裂 | ISO527-2/1A/50 | 17.0 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/7705 |
|---|---|---|---|
| melt mass-flow rate | 230°C/2.16kg | ISO1133 | 22 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/7705 |
|---|---|---|---|
| 1.8MPa,未退火,3.20mm | ASTMD648 | 57.0 °C | |
| vicat | ISO306/A50 | 130 °C | |
| 0.45MPa,未退火,3.20mm | ASTMD648 | 112 °C | |
| Hot deformation temperature 6 | 1.8MPa,Unannealed | ISO75-2/A | 59.0 °C |
| MD：-30到100°C | ISO11359-2 | 5.9E-05 cm/cm/°C | |
| TD：-30to100°C | ISO11359-2 | 1.5E-04 cm/cm/°C | |
| Hot deformation temperature 6 | 0.45MPa,Unannealed | ISO75-2/B | 105 °C |