PA6 B3WG10 BASF SHANGHAI
Ultramid®
Industrial components
High mobility、High rigidity、Heat aging
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF SHANGHAI/B3WG10 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 90 kJ/m² |
| Mechanical properties | Test Condition | Test Method | BASF SHANGHAI/B3WG10 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.5 % |
| bending strength | 23°C | ISO 178 | 345 Mpa |
| Flexural modulus | 23°C | ISO 178 | 14500 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 16700 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 225 Mpa |
| physical property | Test Condition | Test Method | BASF SHANGHAI/B3WG10 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.4 % |
| 饱和,23°C | ISO 62 | 4.8 % |
| Thermal performance | Test Condition | Test Method | BASF SHANGHAI/B3WG10 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 215 °C | |
| melting temperature | ISO 3146 | 220 °C |