PBT Lupox® TE5000GH LG Chem Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG Chem Ltd./Lupox® TE5000GH |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 980 J/m |
| -30°C,3.20mm | ASTM D256 | 200 J/m |
| Mechanical properties | Test Condition | Test Method | LG Chem Ltd./Lupox® TE5000GH |
|---|---|---|---|
| elongation | 断裂,3.20mm | ASTM D638 | >100 % |
| Flexural modulus | 6.40mm | ASTM D790 | 1960 MPa |
| bending strength | 屈服,6.40mm | ASTM D790 | 88.3 MPa |
| tensile strength | 屈服,3.20mm | ASTM D638 | 56.9 MPa |
| physical property | Test Condition | Test Method | LG Chem Ltd./Lupox® TE5000GH |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.70to0.80 % |
| Water absorption rate | 饱和,23°C | ASTM D570 | 0.080 % |
| density | ASTM D792 | 1.21 g/cm³ | |
| melt mass-flow rate | 250°C/5.0kg | ASTM D1238 | 12 g/10min |
| Thermal performance | Test Condition | Test Method | LG Chem Ltd./Lupox® TE5000GH |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 100 °C |
| melting temperature | ASTM D3418 | 223 °C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 115 °C |