PBT 5810G40 MITSUBISHI ENGINEERING JAPAN
NOVADURAN™
Vehicle electronics,Fitness equipment,Bottle cap
Glass fiber reinforced,Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5810G40 |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | 1.E+15 Ω | |
| Volume resistivity | ASTM D257/IEC 60093 | 1.E+14 Ω.cm |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5810G40 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 195 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 10500 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ASTM D638/ISO 527 | 12000 kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5810G40 |
|---|---|---|---|
| purpose | 低翘曲.30%玻纤增强 |
| Physical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5810G40 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.1 % | |
| density | ASTM D792/ISO 1183 | 1.53 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 6 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.08 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5810G40 |
|---|---|---|---|
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 215 ℃（℉） |
| melting temperature | 224 ℃（℉） |