Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM M90-44 TAIWAN POLYPLASTICS
DURACON®
Electrical field、Electronic field、Household appliances、Household appliances
high viscosity、wear resistant、transparent、High mobility、Weather resistance、currency
UL
SGS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TAIWAN POLYPLASTICS/M90-44 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 6.0 kJ/m² |
| hardness | Test Condition | Test Method | TAIWAN POLYPLASTICS/M90-44 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO2039-2 | 80 |
| Supplementary Information | Test Condition | Test Method | TAIWAN POLYPLASTICS/M90-44 |
|---|---|---|---|
| ColorNumber | CF2001/CD3068 |
| Mechanical properties | Test Condition | Test Method | TAIWAN POLYPLASTICS/M90-44 |
|---|---|---|---|
| Wear factor | 0.060MPa,0.15m/sec7 | JISK7218 | 3500 10^-8mm³/N·m |
| 0.98MPa,0.30m/sec5 | JISK7218 | <1.0 10^-8mm³/N·m | |
| Tensile stress | ISO527-2 | 62.0 Mpa | |
| Wear factor | 0.060MPa,0.15m/sec8 | JISK7218 | 6500 10^-8mm³/N·m |
| 0.49MPa,0.30m/sec5 | JISK7218 | <1.0 10^-8mm³/N·m | |
| 0.49MPa,0.30m/sec6 | JISK7218 | 65 10^-8mm³/N·m | |
| Bending stress | ISO178 | 87.0 Mpa | |
| Tensile modulus | ISO527-2 | 2700 Mpa | |
| Nominal tensile fracture strain | ISO527-2 | 35 % | |
| Dynamic2 | JISK7218 | 0.37 | |
| 与钢-动态3 | JISK7218 | 0.46 | |
| Flexural modulus | ISO178 | 2500 Mpa | |
| 与钢-动态4 | JISK7218 | 0.40 | |
| Wear factor | 0.98MPa,0.30m/sec6 | JISK7218 | 30 10^-8mm³/N·m |
| Electrical performance | Test Condition | Test Method | TAIWAN POLYPLASTICS/M90-44 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | 1E+16 ohms | |
| Volume resistivity | IEC60093 | 1E+14 ohms·cm | |
| dielectric strength | 3.00mm | IEC60243-1 | 19 KV/mm |
| flammability | Test Condition | Test Method | TAIWAN POLYPLASTICS/M90-44 |
|---|---|---|---|
| UL flame retardant rating | UL94 | HB |
| physical property | Test Condition | Test Method | TAIWAN POLYPLASTICS/M90-44 |
|---|---|---|---|
| Shrinkage rate | MD:2.00mm | ISO294-4 | 2.0 % |
| melt mass-flow rate | ISO1133 | 9.0 g/10min | |
| Shrinkage rate | TD:2.00mm | ISO294-4 | 2.0 % |
| Melt volume flow rate | 190°C/2.16kg | ISO1133 | 8.00 cm3/10min |
| Water absorption rate | 23°C,24hr | ISO62 | 0.50 % |
| density | ISO1183 | 1.41 g/cm³ | |
| melt mass-flow rate | ASTMD1238 | 9.0 g/10min |
| Thermal performance | Test Condition | Test Method | TAIWAN POLYPLASTICS/M90-44 |
|---|---|---|---|
| 1.8MPa,未退火 | ISO75-2/A | 95.0 °C | |
| MD：23到55°C | 内部方法 | 1.2E-04 cm/cm/°C | |
| TD：23to55°C | 内部方法 | 1.2E-04 cm/cm/°C |