Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP EKC 265N 2 LYONDELLBASELL HOLAND
Hifax
Automotive interior parts、Automotive interior equip、Automotive sector、Application in the automo
scratch resistance 、Stress resistant whitenin、High mobility、Impact resistance、Semi rigid、UV resistance、Mineral reinforcement、enhance、Filler: Mineral filler、20% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LYONDELLBASELL HOLAND/EKC 265N 2 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 0°C | ISO 179/1eU | 无断裂 |
| -30°C | ISO 179/1eU | 35 kJ/m² |
| Mechanical properties | Test Condition | Test Method | LYONDELLBASELL HOLAND/EKC 265N 2 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 18.0 Mpa |
| Tensile modulus | 正割 | ISO 527-2 | 1950 Mpa |
| Flexural modulus | 正割 | ISO 178 | 1900 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 5.0 % |
| physical property | Test Condition | Test Method | LYONDELLBASELL HOLAND/EKC 265N 2 |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 0.90-1.1 % | |
| Melt volume flow rate | 230°C/2.16kg | ISO 1133 | 18.0 cm3/10min |
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 16 g/10min |
| Thermal performance | Test Condition | Test Method | LYONDELLBASELL HOLAND/EKC 265N 2 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 56.0 °C |