Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT POLYlux 3809S POLYKEMI SWEDEN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | POLYKEMI SWEDEN/POLYlux 3809S |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 45 kJ/m² |
| -20°C | ISO 179 | 15 kJ/m² |
| hardness | Test Condition | Test Method | POLYKEMI SWEDEN/POLYlux 3809S |
|---|---|---|---|
| Shore hardness | 邵氏D,15秒 | ASTM D2240 | 76 |
| Mechanical properties | Test Condition | Test Method | POLYKEMI SWEDEN/POLYlux 3809S |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 2000 MPa |
| tensile strength | ISO 527-2 | 50.0 MPa | |
| Tensile strain | 屈服 | ISO 527-2 | 6.0 % |
| bending strength | ISO 178 | 70.0 MPa |
| flammability | Test Condition | Test Method | POLYKEMI SWEDEN/POLYlux 3809S |
|---|---|---|---|
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 750 °C |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | POLYKEMI SWEDEN/POLYlux 3809S |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.70to1.0 % |
| MD | ISO 294-4 | 0.70to1.0 % | |
| density | ISO 1183 | 1.17 g/cm³ |
| Thermal performance | Test Condition | Test Method | POLYKEMI SWEDEN/POLYlux 3809S |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 90.0 °C |
| vicat | -- | ISO 306/A50 | 132 °C |
| -- | ISO 306/B50 | 108 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 81.0 °C |