TSU RapidVac™ VA-1805 Innovative Polymers, Inc.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Uncured Properties | Test Condition | Test Method | Innovative Polymers, Inc./RapidVac™ VA-1805 |
|---|---|---|---|
| Viscosity | 固化时间5 | 25 hr | |
| 25°C4 | 4.5 Pa·s | ||
| GelTime | 4.0to6.0 min | ||
| 25°C2 | 0.55 Pa·s | ||
| 25°C3 | 1.8 Pa·s |
| thermosetting | Test Condition | Test Method | Innovative Polymers, Inc./RapidVac™ VA-1805 |
|---|---|---|---|
| Thermosetting components | 脱模时间 | 30to60 min | |
| 硬化法 | 按重量计算的混合比:100按容量计算的混合比:100 | ||
| 树脂 | 按重量计算的混合比:80按容量计算的混合比:72 |
| Cured Properties | Test Condition | Test Method | Innovative Polymers, Inc./RapidVac™ VA-1805 |
|---|---|---|---|
| tear strength | ASTM D624 | 14.0 kN/m | |
| elongation | 断裂 | ASTM D638 | 100 % |
| tensile strength | ASTM D638 | 6.21 MPa | |
| Shore hardness | ShoreA | ASTM D2240 | 70to80 |
| physical property | Test Condition | Test Method | Innovative Polymers, Inc./RapidVac™ VA-1805 |
|---|---|---|---|
| density | 基体树脂 | 1.21 g/cm³ | |
| Hardener | 1.14 g/cm³ | ||
| Shrinkage rate | MD | ASTM D2566 | 0.20to0.50 % |
| density | Cured | 1.12 g/cm³ |