Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 73G15T DUPONT USA
Zytel®
Automotive components、Industrial machinery
Thermal stability、High crystallinity、Filler: Glass fiber reinf、15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/73G15T |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 80 kJ/m² |
| Electrical performance | Test Condition | Test Method | DUPONT USA/73G15T |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| Dissipation Factor | 100Hz | IEC 60250 | 0.016 |
| 1MHz | IEC 60250 | 0.016 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/73G15T |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 5000 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 5.0 % |
| tensile strength | 断裂 | ISO 527-2 | 100 Mpa |
| Poisson's ratio | ISO 527 | -- |
| flammability | Test Condition | Test Method | DUPONT USA/73G15T |
|---|---|---|---|
| FMVSS flammability | FMVSS302 | B | |
| Limiting Oxygen Index | ISO 4589-2 | 25 % | |
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |
| physical property | Test Condition | Test Method | DUPONT USA/73G15T |
|---|---|---|---|
| MeltViscosity | 280°C,1000sec^-1 | ISO 11443 | 300000 mPa·s |
| Shrinkage rate | TD | ISO 294-4 | 1.2 % |
| MD | ISO 294-4 | 0.70 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 7.5 % |
| 平衡,23°C,2.00mm,50%RH | ISO 62 | 2.4 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/73G15T |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 221 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 215 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 190 °C | |
| Glass Transition Temperature | ISO 11357-2 | 60.0 °C |