PC EGN2020KR MITSUBISHI ENGINEERING JAPAN
IUPILON™
Fiber grade
Flame retardant,enhance,High mobility,Filler: Glass fiber reinf,20% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EGN2020KR |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 39 kJ/m² |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EGN2020KR |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EGN2020KR |
|---|---|---|---|
| bending strength | ISO 178 | 139 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.9 % |
| Flexural modulus | ISO 178 | 5500 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 90.0 Mpa |
| flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EGN2020KR |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-2 |
| 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EGN2020KR |
|---|---|---|---|
| Shrinkage rate | TD:3.20mm | 0.25-0.45 % | |
| MD:3.20mm | 0.15-0.35 % | ||
| Water absorption rate | 饱和,23°C | ISO 62 | 0.11 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EGN2020KR |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 141 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 137 °C |