ABS PA-763 TAIWAN CHIMEI
POLYLAC® 
Electronic field、Electrical field
Flame retardant
UL
MSDS
RoHS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodTAIWAN CHIMEI/PA-763
Charpy Notched Impact Strength23°CISO 17922 kJ/m²
Impact strength of cantilever beam gap23°C,3.20mmASTM D256230 J/m
23°C,6.40mmASTM D256200 J/m
Charpy Notched Impact Strength-30°CISO 17912 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A11 kJ/m²
23°CISO 180/1A21 kJ/m²
hardnessTest ConditionTest MethodTAIWAN CHIMEI/PA-763
Rockwell hardnessR级ASTM D78598
Mechanical propertiesTest ConditionTest MethodTAIWAN CHIMEI/PA-763
elongation断裂4ASTM D63830 %
bending strength--5ASTM D79060.7 Mpa
tensile strength 屈服4ASTM D63838.6 Mpa
屈服ISO 527-2/5038.0 Mpa
bending strength--6ISO 17858.0 Mpa
elongation断裂ISO 527-2/5015 %
Flexural modulus--6ISO 1782000 Mpa
--5ASTM D7902410 Mpa
tensile strength 断裂ISO 527-2/5029.0 Mpa
flammabilityTest ConditionTest MethodTAIWAN CHIMEI/PA-763
UL flame retardant rating2.5mmUL 945VA
1.5mmUL 94V-0
physical property Test ConditionTest MethodTAIWAN CHIMEI/PA-763
density23°CISO 11831.19 g/cm³
melt mass-flow rate200°C/5.0kgASTM D12382.8 g/10min
Shrinkage rateISO 294-40.30-0.60 %
density--3ASTM D7921.19 g/cm³
Melt volume flow rate220°C/10.0kgISO 113327.0 cm3/10min
Thermal performanceTest ConditionTest MethodTAIWAN CHIMEI/PA-763
Heat distortion temperature1.8MPa,未退火，HDTASTM D64885.0 °C
vicat--ASTM D15257104 °C
--ISO 306/A50103 °C
Heat distortion temperature1.8MPa,未退火，HDTISO 75-2/A86.0 °C
vicat--ISO 306/B5096.0 °C
Linear coefficient of thermal expansionMDISO 11359-28.5E-05 cm/cm/°C
Heat distortion temperature1.8MPa,退火，HDTASTMD64896.0 °C