Product Name
Brand Name
Usages
Properties
Certificates
PPA UFL-4036 HS SABIC INNOVATIVE US
LNP™ LUBRICOMP™
tubing、Lighting applications
Thermal stability、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/UFL-4036 HS |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 47 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 8.90 J |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 2.00 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 9.1 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/UFL-4036 HS |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 15400 Mpa |
| ISO 527-2/1 | 12600 Mpa | ||
| tensile strength | 断裂 | ISO 527-2/5 | 192 Mpa |
| Tensile modulus | --3 | ASTM D638 | 15400 Mpa |
| elongation | 屈服 | ASTM D638 | 1.8 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 2.0 % |
| bending strength | Break,50.0mmSpan | ASTM D790 | 233 Mpa |
| Flexural modulus | 50.0mmSpan | ASTM D790 | 10600 Mpa |
| Wear factor | Washer | ASTM D3702Modified | 5.00 10^-10in^5-min/ft-lb-hr |
| tensile strength | 屈服 | ISO 527-2/5 | 192 Mpa |
| elongation | 断裂 | ASTM D638 | 1.7 % |
| tensile strength | Break | ASTM D638 | 189 Mpa |
| bending strength | Yield,50.0mmSpan | ASTM D790 | 242 Mpa |
| coefficient of friction | Static | ASTM D3702Modified | 0.52 |
| Flexural modulus | ISO 178 | 11300 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.0 % |
| Wear factor | Ring | ASTM D3702Modified | 0.100 10^-10in^5-min/ft-lb-hr |
| tensile strength | 屈服 | ASTM D638 | 189 Mpa |
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.48 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/UFL-4036 HS |
|---|---|---|---|
| Shrinkage rate | MD：24小时 | ASTM D955 | 0.20-0.40 % |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.15 % |
| 平衡,23°C,50%RH | ISO 62 | 0.25 % | |
| Shrinkage rate | TD：24hr | ASTM D955 | 0.80-1.0 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/UFL-4036 HS |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTM D696 | 2.1E-05 cm/cm/°C |
| TD：-30to30°C | ASTM D696 | 4.5E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 273 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 277 °C |