Ethylene Copolymer TOTAL Polyethylene EVA 1005 VN 2 TOTAL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Test Condition | Test Method | TOTAL/TOTAL Polyethylene EVA 1005 VN 2 | |
|---|---|---|---|
| tensile strength | TD:屈服,40µm,吹塑薄膜 | ISO 527-3 | 8.50 MPa |
| MD:屈服,40µm,吹塑薄膜 | ISO 527-3 | 9.50 MPa | |
| vicat | ISO 306 | 90.0 °C | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 0.50 g/10min |
| Elmendorf tear strength | TD:40µm,吹塑薄膜 | ISO 6383-2 | 33 N |
| density | ISO 1183 | 0.925 g/cm³ | |
| melting temperature | ISO 11357-3 | 104 °C | |
| film thickness | 40 µm | ||
| Tensile modulus | ISO 527-2 | 160 MPa | |
| Dart impact | 40µm,吹塑薄膜 | ISO 7765-1 | 340 g |
| tensile strength | MD:断裂,40µm,吹塑薄膜 | ISO 527-3 | 32.0 MPa |
| Haze ratio | 40.0µm,吹塑薄膜 | ISO 14782 | 8.8 % |
| elongation | TD:断裂,40µm,吹塑薄膜 | ISO 527-3 | 570 % |
| Elmendorf tear strength | MD:40µm,吹塑薄膜 | ISO 6383-2 | 34 N |
| elongation | MD:断裂,40µm,吹塑薄膜 | ISO 527-3 | 300 % |
| Vinyl acetate content | 内部方法 | 5.5 wt% | |
| tensile strength | TD:断裂,40µm,吹塑薄膜 | ISO 527-3 | 27.0 MPa |