Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LCP 6140L DUPONT USA
ZENITE®
--
High impact resistance、High lubrication
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | DUPONT USA/6140L |
|---|---|---|---|
| Thickness Tested | UL 94 | 0.75 mm | |
| Grade @ Thickness | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/6140L |
|---|---|---|---|
| elongation at break | 3.2mm | ASTM D-638 | 1.3 % |
| Flexural modulus | 3.2mm | ASTM D-790 | 15600 Mpa |
| tensile strength | 3.2mm | ASTM D-638 | 135 Mpa |
| Impact strength of cantilever beam gap | 3.2mm | ASTM D-256 | 80 J/m |
| bending strength | 3.2mm | ASTM D-790 | 182 Mpa |
| Thermal performance | Test Condition | Test Method | DUPONT USA/6140L |
|---|---|---|---|
| RTI Imp | 3.0MPa | UL 746-B | 220 °C |
| melting temperature | ASTM D-3418 | 335 °C | |
| Glass Transition Temperature | ASTM D-3418 | 120 °C | |
| RTI Imp | 3.0mm | UL 746-B | 240 °C |
| melting temperature | 350-360 °C | ||
| RTI Imp | 1.5mm | UL 746-B | 240 °C |
| RTI Elec | 3.0mm | UL 746-B | 240 °C |
| 1.5mm | UL 746-B | 240 °C | |
| Temperature range for molding | 30-95 °C | ||
| RTI Imp | 0.8mm | UL 746-B | 240 °C |
| Heat distortion temperature | 1.80MPa，HDT | ASTM D-648 | 271 °C |
| RTI Elec | 0.8mm | UL 746-B | 240 °C |
| drying temperature | 135 °C |