Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS CX2244ME-111 SABIC INNOVATIVE SHANGHAI
CYCOLOY™ 
Electronic and electrical accessories,Automotive components
Low temperature resistanc,High sliding
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

thermal performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/CX2244ME-111
Ball Pressure Test73 to 77°CIEC 60695-10-2通过
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D64889.0 °C
1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9ISO 75-2/Af93.0 °C
Linear coefficient of thermal expansionAcross Flow : -40 to 40°CASTM E8317.5E-5 cm/cm/°C
Across Flow : -40°CISO 11359-27.5E-5 cm/cm/°C
Flow : -40 to 40°CASTM E8317.5E-5 cm/cm/°C
RTIUL 74690.0 °C
RTI ElecUL 74690.0 °C
RTI ImpUL 74690.0 °C
Vicat softening temperature--ISO 306/B120113 °C
--ASTM D152510110 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/CX2244ME-111
Bending modulus--5ISO 1782500 Mpa
50.0 mm Span4ASTM D7902500 Mpa
bending strengthYield, 50.0 mm Span4ASTM D790104 Mpa
--5,6ISO 17896.0 Mpa
elongationYieldISO 527-2/504.0 %
Yield3ASTM D6384.1 %
Break3ASTM D638100 %
BreakISO 527-2/5090 %
Tensile modulus--2ASTM D6382600 Mpa
--ISO 527-2/12600 Mpa
tensile strengthYieldISO 527-2/5065.0 Mpa
BreakISO 527-2/5050.0 Mpa
Break3ASTM D63858.0 Mpa
Yield3ASTM D63865.0 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/CX2244ME-111
Compared to the anti leakage trace indexUL 746PLC 3
High arc combustion indexUL 746PLC 0
Hot wire ignitionUL 746PLC 3
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/CX2244ME-111
melt mass-flow rate260°C/2.16 kgASTM D123818 g/10 min
Melt Volume Flow Rate (MVR)260°C/2.16 kgISO 113315.0 cm3/10min
Shrinkage rate3.20 mm，FlowInternal Method0.40 - 0.60 %
Water absorption rateSaturation, 23°CISO 620.20 %
Equilibrium, 23°C, 50% RHISO 620.10 %
impact performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/CX2244ME-111
Charpy Notched Impact Strength23°CISO 179/1eA40 kJ/m²
-30°CISO 179/1eA10 kJ/m²
Dart impact23°C, Total EnergyASTM D376365.0 J
flammabilityTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/CX2244ME-111
Burning wire flammability index3.0 mmIEC 60695-2-12960 °C
Hot filament ignition temperature3.0 mmIEC 60695-2-13800 °C
UL flame retardant rating0.75 mmUL 94V-0
1.5 mmUL 945VB
injectionTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/CX2244ME-111
drying temperature80 to 90 °C
drying time2.0 to 4.0 hr
Exhaust hole depth0.030 to 0.075 mm
Hopper temperature60 to 80 °C
Mold temperature60 to 85 °C
Processing (melt) temperature250 to 300 °C
Spray nozzle temperature250 to 300 °C
Suggested maximum moisture content0.020 %
Temperature at the front of the material cylinder250 to 300 °C
Temperature at the rear of the barrel230 to 280 °C
Temperature in the middle of the barrel240 to 290 °C