ABS PA-777E TAIWAN CHIMEI
POLYLAC® 
Home appliance components、Electronic field、Electrical field、Automotive sector
Medium impact resistance、heat-resisting
MSDS
RoHS
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodTAIWAN CHIMEI/PA-777E
Charpy Notched Impact Strength23°CISO 17913 kJ/m²
Impact strength of cantilever beam gap23°C,3.20mmASTM D256120 J/m
23°C,6.40mmASTM D256110 J/m
Charpy Notched Impact Strength-30°CISO 1796.0 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A6.0 kJ/m²
23°CISO 180/1A12 kJ/m²
hardnessTest ConditionTest MethodTAIWAN CHIMEI/PA-777E
Rockwell hardnessR级ASTM D785115
Mechanical propertiesTest ConditionTest MethodTAIWAN CHIMEI/PA-777E
tensile strength 屈服4ASTM D63844.0 Mpa
屈服ISO 527-2/5045.0 Mpa
elongation断裂4ASTM D63810 %
bending strength--5ASTM D79068.3 Mpa
--6ISO 17874.0 Mpa
elongation断裂ISO 527-2/5029 %
Flexural modulus--6ISO 1782300 Mpa
--5ASTM D7902210 Mpa
tensile strength 断裂ISO 527-2/5032.0 Mpa
flammabilityTest ConditionTest MethodTAIWAN CHIMEI/PA-777E
UL flame retardant rating1.5mmUL 94HB
physical property Test ConditionTest MethodTAIWAN CHIMEI/PA-777E
density23°CISO 11831.07 g/cm³
Shrinkage rateISO 294-40.30-0.60 %
density--3ASTM D7921.07 g/cm³
melt mass-flow rate220°C/10.0kgASTM D12384.0 g/10min
Melt volume flow rate220°C/10.0kgISO 11334.50 cm3/10min
Thermal performanceTest ConditionTest MethodTAIWAN CHIMEI/PA-777E
Heat distortion temperature1.8MPa,未退火，HDTASTM D648109 °C
1.8MPa,退火，HDTASTM D648120 °C
1.8MPa,退火，HDTISO 75-2/A121 °C
1.8MPa,未退火，HDTISO 75-2/A101 °C
vicat--ASTMD15257129 °C
--ISO 306/B50121 °C
Linear coefficient of thermal expansionMDISO 11359-28.2E-05 cm/cm/°C