PE Copolymer LITEN ZB 29 Unipetrol RPA, s.r.o.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | Unipetrol RPA, s.r.o./LITEN ZB 29 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179 | 11 kJ/m² |
-30°C | ISO 179 | 5.0 kJ/m² |
Supplementary Information | Test Condition | Test Method | Unipetrol RPA, s.r.o./LITEN ZB 29 |
---|---|---|---|
Blow molding mold temperature | 20to30 °C | ||
Blow molding melt temperature | 180to220 °C |
hardness | Test Condition | Test Method | Unipetrol RPA, s.r.o./LITEN ZB 29 |
---|---|---|---|
Shore hardness | 邵氏D | ISO 868 | 60 |
Mechanical properties | Test Condition | Test Method | Unipetrol RPA, s.r.o./LITEN ZB 29 |
---|---|---|---|
Tensile strain | 屈服 | ISO 527-2 | 10 % |
tensile strength | 屈服 | ISO 527-2 | 25.0 MPa |
Flexural modulus | ISO 178 | 1100 MPa |
physical property | Test Condition | Test Method | Unipetrol RPA, s.r.o./LITEN ZB 29 |
---|---|---|---|
density | 23°C | ISO 1183 | 0.952 g/cm³ |
melt mass-flow rate | 190°C/5.0kg | ISO 1133 | 1.2 g/10min |
Environmental stress cracking resistance | F50 | ASTM D1693 | 250 hr |
melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 0.20 g/10min |
Melt flow ratio | 21,6/2,16 | 100 | |
melt mass-flow rate | 190°C/21.6kg | ISO 1133 | 24 g/10min |
Thermal performance | Test Condition | Test Method | Unipetrol RPA, s.r.o./LITEN ZB 29 |
---|---|---|---|
melting temperature | ISO 11357-3 | 130 °C | |
vicat | ISO 306 | 124 °C | |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 45.0 °C |