| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/767 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 15 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 105 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | 屈服 | ISO 527-2/5 | 69.9 Mpa |
| Flexural modulus | ASTM D790/ISO 178 | 3430 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ISO 178 | 130 Mpa | |
| Flexural modulus | ISO 178 | 3700 Mpa | |
| elongation at break | ASTM D638/ISO 527 | 2.0 % | |
| Rockwell hardness | ASTM D785 | 83 | |
| tensile strength | ASTM D638/ISO 527 | 72 kg/cm²(MPa)[Lb/in²] |
| Physical properties | Test Condition | Test Method | ASAHI JAPAN/767 |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238/ISO 1133 | 12.5 g/10min | |
| density | ASTM D792/ISO 1183 | 1.08 kg·cm/cm(J/M)ft·lb/in |
| flammability | Test Condition | Test Method | ASAHI JAPAN/767 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | ASAHI JAPAN/767 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.40-0.60 % |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 13.0 cm3/10min |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 12 g/10min |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/767 |
|---|---|---|---|
| vicat | ISO 306/B | 103 °C | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 90 ℃（℉） |
| vicat | ASTM D1525/ISO R306 | 110 ℃（℉） | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 87.7 °C |
| RTI Imp | UL 746 | 50.0 °C | |
| RTI | UL 746 | 50.0 °C | |
| ball-indentation hardness | EMAC | 95 °C | |
| RTI Elec | UL 746 | 50.0 °C |