Fluorelastomer G-912 DAIKIN INDUSTRIES, Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | DAIKIN INDUSTRIES, Ltd./G-912 |
|---|---|---|---|
| cure temperature | 160 °C | ||
| Tryst | TR10 | -8 °C | |
| Curing Time | Curelastometer法 | 3.0 min | |
| GehmanTorsion Test | T2 | -2 °C | |
| Tryst | TR70 | -2 °C | |
| GehmanTorsion Test | T10 | -5 °C |
| hardness | Test Condition | Test Method | DAIKIN INDUSTRIES, Ltd./G-912 |
|---|---|---|---|
| Shore hardness | 邵氏A,25°C | 73 |
| elastomer | Test Condition | Test Method | DAIKIN INDUSTRIES, Ltd./G-912 |
|---|---|---|---|
| tensile strength | 100%应变,25°C | 8.50 MPa | |
| elongation | 断裂,25°C | 170 % | |
| compression set | 175°C,70hr | 11 % | |
| 200°C,70hr | 16 % | ||
| 25°C,70hr | 7.0 % | ||
| 100°C,70hr | 6.0 % | ||
| tensile strength | 屈服,25°C | 20.0 MPa | |
| tear strength | 25°C | 17.6 kN/m |
| aging | Test Condition | Test Method | DAIKIN INDUSTRIES, Ltd./G-912 |
|---|---|---|---|
| Change rate of hardness (Shore) in the air | 邵氏A,230°C,70hr | 0.0 | |
| Change rate of ultimate elongation in air | 230°C,70hr | 12 % | |
| Change rate of tensile strength in air | 230°C,70hr | -13 % |
| physical property | Test Condition | Test Method | DAIKIN INDUSTRIES, Ltd./G-912 |
|---|---|---|---|
| Mooney viscosity | ML1+10,121°C | 56 MU | |
| density | 1.87to1.91 g/cm³ | ||
| Fluorine content | 71 % |
| Thermal performance | Test Condition | Test Method | DAIKIN INDUSTRIES, Ltd./G-912 |
|---|---|---|---|
| brittle temperature | -20.0 °C |