Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

POM FS410 ASAHI JAPAN
TENAC™
bearing
High sliding,wear resistant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/FS410 |
---|---|---|---|
Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 39 kg·cm/cm(J/M)ft·lb/in | |
bending strength | ASTM D790/ISO 178 | 98 kg/cm²(MPa)[Lb/in²] | |
Flexural modulus | ASTM D790/ISO 178 | 2940 kg/cm²(MPa)[Lb/in²] | |
Rockwell hardness | ASTM D785 | 94 M | |
bending strength | ASTM D790 | 98 Mpa | |
elongation at break | ASTM D638/ISO 527 | 30 % | |
Rockwell hardness | ASTM D785 | 94 | |
Impact strength of cantilever beam gap | ASTM D256 | 39 J/m | |
tensile strength | ASTM D638/ISO 527 | 67 kg/cm²(MPa)[Lb/in²] | |
elongation at break | ASTM D638 | 30 % | |
Flexural modulus | ASTM D790 | 2940 Mpa | |
tensile strength | ASTM D638 | 67 Mpa |
Physical properties | Test Condition | Test Method | ASAHI JAPAN/FS410 |
---|---|---|---|
Shrinkage rate | ASTM D955 | 1.8-2.2 % | |
density | ASTM D792/ISO 1183 | 1.42 | |
melt mass-flow rate | ASTM D1238/ISO 1133 | 9 g/10min | |
Water absorption rate | ASTM D570/ISO 62 | 0.2 % |
physical property | Test Condition | Test Method | ASAHI JAPAN/FS410 |
---|---|---|---|
Shrinkage rate | 垂直方向 | 旭化成法 | 1.8-2.2 % |
平行方向 | 旭化成法 | 1.8-2.2 % | |
Water absorption rate | ASTM D570 | 0.2 % |
Thermal performance | Test Condition | Test Method | ASAHI JAPAN/FS410 |
---|---|---|---|
melt mass-flow rate | ASTM D1238 | 9 g/10min | |
Heat distortion temperature | HDT | ASTM D648/ISO 75 | 136 ℃(℉) |
0.45MPa,HDT | ASTM D648 | 170 °C | |
1.82MPa,HDT | ASTM D648 | 136 °C | |
UL flame retardant rating | UL 94 | HB | |
Linear coefficient of thermal expansion | TMA法 | 10 |