Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

PA66 DUPONT USA 101F-NC010

Injection grade

US$ 3,540 / MT

FOB Guangzhou port, China

Physical properties	Test Condition	Test Method	DUPONT USA/101F-NC010
Shrinkage rate	TD:80°C,48hr	ISO 294-4	0.10 %
density		ISO 1183	1.14 g/cm³
Shrinkage rate	MD	ISO 294-4	1.4 %
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	8.5 %
Top out temperature			190 °C
SpecificHeatCapacity of Melt			2790 J/kg/°C
Shrinkage rate	TD	ISO 294-4	1.4 %
Shrinkage rate		MD:80°C,48hr	ISO 294-4	0.20 %
MediumDensity			0.970 g/cm³
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	2.6 %
ThermalConductivityofMelt			0.16 W/m/K
Stickiness		ISO 307	140 cm³/g
mechanical properties	Test Condition	Test Method	DUPONT USA/101F-NC010
Tensile creep modulus	1hr	ISO 899-1	-- Mpa
Tensile modulus		ISO 527-2	3100 Mpa
Nominal tensile fracture strain		ISO 527-2	20 %
Bending modulus		ISO 178	2800 Mpa
Tensile creep modulus	1000hr	ISO 899-1	-- Mpa
Tensile strain	Yield	ISO 527-2	4.5 %
tensile strength	Yield	ISO 527-2	82.0 Mpa
flammability	Test Condition	Test Method	DUPONT USA/101F-NC010
UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	V-2
Extreme Oxygen Index		ISO 4589-2	28 %
UL flame retardant rating	1.5mm	UL 94	V-2
UL flame retardant rating		0.71mm	IEC 60695-11-10,-20	V-2
Fogging-G-value	condensate	ISO 6452	1E-04 g
FMVSS flammability		FMVSS302	SE
Electrical performance	Test Condition	Test Method	DUPONT USA/101F-NC010
Dissipation factor	100Hz	IEC 60250	0.014
Volume resistivity		IEC 60093	1E+15 ohms·cm
Dissipation factor	1MHz	IEC 60250	0.018
Relative permittivity	100Hz	IEC 60250	3.80
Relative permittivity		1MHz	IEC 60250	3.60
Dielectric strength		IEC 60243-1	32 KV/mm
Supplementary Information	Test Condition	Test Method	DUPONT USA/101F-NC010
Odor		VDA270	3.00
EmissionofOrganicCompounds		VDA277	6.50 µgC/g
impact performance	Test Condition	Test Method	DUPONT USA/101F-NC010
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	400 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	300 kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	4.5 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	5.5 kJ/m²
Impact strength of cantilever beam gap		-40°C	ISO 180/1A	5.5 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Charpy Notched Impact Strength	23°C	ISO 179/1eA	6.0 kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	6.0 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	300 kJ/m²
film	Test Condition	Test Method	DUPONT USA/101F-NC010
Tensile strain	Yield，MD	ISO 527-3	4.5 %
thermal performance	Test Condition	Test Method	DUPONT USA/101F-NC010
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	70.0 °C
Melting temperature		ISO 11357-3	262 °C
Vicat softening temperature		ISO 306/B50	240 °C
Effective thermal diffusivity coefficient			5E-08 m²/s
Linear coefficient of thermal expansion	MD	ISO 11359-2	1E-04 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	190 °C
Glass transition temperature		ISO 11357-2	60.0 °C
Linear coefficient of thermal expansion	TD	ISO 11359-2	1.1E-04 cm/cm/°C