PA6 Nycast SLX Cast Nylons Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Cast Nylons Ltd./Nycast SLX |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 74to80 J/m |
| hardness | Test Condition | Test Method | Cast Nylons Ltd./Nycast SLX |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 75to84 |
| Rockwell hardness | R级 | ASTM D785 | 113to120 |
| Mechanical properties | Test Condition | Test Method | Cast Nylons Ltd./Nycast SLX |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 38to47 % |
| tensile strength | ASTM D638 | 69.6to70.3 MPa | |
| Heat distortion temperature | HDT | ASTM D621 | 0.510 % |
| compressive strength | ASTM D695 | 101to112 MPa | |
| coefficient of friction | 与自身-动态 | ASTM D1894 | 0.14to0.19 |
| Tensile modulus | ASTM D638 | 3170 MPa | |
| Flexural modulus | ASTM D790 | 2510to2590 MPa | |
| Compression Modulus | ASTM D695 | 1870to1970 MPa | |
| bending strength | ASTM D790 | 86.9to89.6 MPa | |
| coefficient of friction | 与自身-静态 | ASTM D1894 | 0.12to0.14 |
| shear strength | ASTM D732 | 58.9to59.2 MPa |
| physical property | Test Condition | Test Method | Cast Nylons Ltd./Nycast SLX |
|---|---|---|---|
| Water absorption rate | 24hr | ASTM D570 | 0.032 % |
| density | ASTM D792 | 1.12to1.14 g/cm³ |
| Thermal performance | Test Condition | Test Method | Cast Nylons Ltd./Nycast SLX |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 70.0to72.2 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 216 °C | |
| 熔融温度，HDT | ASTM D648 | 221 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 7.5E-05 cm/cm/°C |