Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LDPE LT750 PCC IRAN
--
film、Bag、Handbag、film、chip
low density、optical performance 、antioxidant、Moderate resistance to cl、Moderate smoothness、Antioxidant function、Moderate anti sticking、Moderate smoothing agent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | PCC IRAN/LT750 |
|---|---|---|---|
| density | ASTM D-1505 | 0.920 g/cm³ | |
| melt mass-flow rate | 190℃/2.16kg | ASTM D-1238 | 6.5 g/10min |
| film thickness | 50 µm |
| Mechanical properties | Test Condition | Test Method | PCC IRAN/LT750 |
|---|---|---|---|
| tensile strength | 50.0µm，屈服,MD | ASTM D-882 | 11 Mpa |
| Dart impact | 50.0µm | ASTM D-1709 | 130 g |
| Elmendorf tear strength | 50.0µm，TD | ASTM D-1922 | 3.6 g |
| coefficient of friction | ASTM D-1894 | 0.10 | |
| tensile strength | 50.0µm，MD,断裂 | ASTM D-882 | 29 Mpa |
| 50.0µm，屈服,TD | ASTM D-882 | 12 Mpa | |
| 50.0µm，TD,断裂 | ASTM D-882 | 25 Mpa | |
| elongation at break | 50.0µm，TD | ASTM D-882 | 440 % |
| Elmendorf tear strength | 50.0µm，MD | ASTM D-1922 | 4.4 g |
| elongation at break | 50.0µm，MD | ASTM D-882 | 270 % |
| optical performance | Test Condition | Test Method | PCC IRAN/LT750 |
|---|---|---|---|
| transparency | 30.0µm | ASTM D-1746 | 42 |
| gloss | 30.0µm | ASTM D-2457 | 59 |
| Haze ratio | 50.0µm | ASTM D-1003 | 9.7 % |
Contact Us
Get App
Top