Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS MB8900 MITSUBISHI ENGINEERING JAPAN
IUPILON™
Shell,Electronic and Electrical Applications
heat-resisting,High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB8900 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 无断裂 |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB8900 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2800 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 44 % | |
| bending strength | ISO 178 | 88.0 Mpa | |
| Flexural modulus | ISO 178 | 2600 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 3.5 % |
| tensile strength | 屈服 | ISO 527-2 | 55.0 Mpa |
| flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB8900 |
|---|---|---|---|
| UL flame retardant rating | 1.00mm | UL 94 | V-1 |
| 1.50mm | UL 94 | 5VB |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB8900 |
|---|---|---|---|
| Shrinkage rate | TD:3.20mm | 0.25-0.45 % | |
| 吸水率(饱和,23°C) | 0.20 % | ||
| Melt volume flow rate | 260°C/2.16kg | ISO 1133 | 23.0 cm3/10min |
| Shrinkage rate | MD:3.20mm | 0.25-0.45 % | |
| melt mass-flow rate | 260°C/2.16kg | ISO 1133 | 25 g/10min |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB8900 |
|---|---|---|---|
| 1.8MPa, Not annealed | ISO 75-2/A | 77.0 °C | |
| 0.45MPa, Not annealed | ISO 75-2/B | 86.0 °C |