TP, Unspecified Ultralloy™ 51 HAPCO USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | HAPCO USA/Ultralloy™ 51 |
---|---|---|---|
Suspended wall beam without notch impact strength | ASTM D256 | >110 J/m | |
Impact strength of cantilever beam gap | ASTM D256 | >110 J/m |
hardness | Test Condition | Test Method | HAPCO USA/Ultralloy™ 51 |
---|---|---|---|
Shore hardness | 邵氏D | ASTM D2240 | 76 |
Mechanical properties | Test Condition | Test Method | HAPCO USA/Ultralloy™ 51 |
---|---|---|---|
elongation | 断裂 | ASTM D638 | 13 % |
tensile strength | ASTM D638 | 39.6 MPa | |
Tensile modulus | ASTM D638 | 862 MPa | |
Flexural modulus | ASTM D790 | 1320 MPa | |
bending strength | ASTM D790 | 54.5 MPa |
thermosetting | Test Condition | Test Method | HAPCO USA/Ultralloy™ 51 |
---|---|---|---|
Thermosetting mixed viscosity | 25°C | ASTM D4878 | 240 cP |
GelTime | 25°C | ASTM D2971 | 8.5 min |
stripping time | 21°C | 内部方法 | 45to90 min |
Thermosetting components | 部件A | 按重量计算的混合比:100.按容量计算的混合比:100 | |
部件B | 按重量计算的混合比:100.按容量计算的混合比:120 |
physical property | Test Condition | Test Method | HAPCO USA/Ultralloy™ 51 |
---|---|---|---|
Shrinkage rate | MD | ASTM D2566 | 0.10to0.40 % |
density | ASTM D4669 | 1.10 g/cm³ | |
Weight Percubicinch | 18 g |
Thermal performance | Test Condition | Test Method | HAPCO USA/Ultralloy™ 51 |
---|---|---|---|
Heat distortion temperature | 0.45MPa,未退火,HDT | ASTM D648 | 60.0 °C |