PA66 AR218V30 BK SOLVAY SHANGHAI
--
--
High impact resistance、Glass fiber reinforced、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY SHANGHAI/AR218V30 BK |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 6.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 45 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SOLVAY SHANGHAI/AR218V30 BK |
|---|---|---|---|
| Tensile modulus | 23°C | ISO 527-2/1A | 9900 Mpa |
| Tensile strain | 断裂, 23°C | ISO 527-2 | 2.4 % |
| bending strength | 23°C | ISO 178 | 200 Mpa |
| Flexural modulus | 23°C | ISO 178 | 7000 Mpa |
| bending strength | 23°C | ASTM D790 | 220 Mpa |
| tensile strength | 断裂, 23°C | ISO 527-2/1A | 150 Mpa |
| flammability | Test Condition | Test Method | SOLVAY SHANGHAI/AR218V30 BK |
|---|---|---|---|
| UL flame retardant rating | 1.6 mm | UL 94 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 23 % | |
| Burning wire flammability index | 1.6 mm | IEC 60695-2-12 | 650 °C |
| physical property | Test Condition | Test Method | SOLVAY SHANGHAI/AR218V30 BK |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 1.7 % |
| 24 hr, 23°C | ISO 62 | 0.80 % | |
| 饱和, 23°C | ISO 62 | 5.3 % |
| Thermal performance | Test Condition | Test Method | SOLVAY SHANGHAI/AR218V30 BK |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/Bf | 240 °C |
| melting temperature | ISO 11357-3 | 260 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/Af | 235 °C |
| injection | Test Condition | Test Method | SOLVAY SHANGHAI/AR218V30 BK |
|---|---|---|---|
| Suggested maximum moisture content | 0.20 % | ||
| Temperature in the middle of the barrel | 275 to 285 °C | ||
| Temperature at the rear of the barrel | 270 to 280 °C | ||
| drying temperature | 80 °C | ||
| Temperature at the front of the material cylinder | 280 to 290 °C | ||
| Temperature | 70 to 100 °C |