Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC DFL-4534 BK SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electronic and Electrical、Lighting applications
Easy to form、Easy to demould
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4534 BK |
|---|---|---|---|
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ASTM E831, ISO 11359-2 | 4.7E-5 cm/cm/°C |
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 3 | ISO 75-2/Bf | 145 °C |
| Linear thermal expansion coefficient | 横向 : -40 到 40°C | ASTM E831 | 3.6E-5 cm/cm/°C |
| 横向 : -40°C | ISO 11359-2 | 3.6E-5 cm/cm/°C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 141 °C |
| 0.45 MPa, 未退火, 3.20 mm | 143 °C | ||
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 3 | ISO 75-2/Af | 141 °C |
| Injection | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4534 BK |
|---|---|---|---|
| Suggested Max Moisture | 0.020 % | ||
| Middle Temperature | 310 到 320 °C | ||
| Processing (Melt) Temp | 305 到 325 °C | ||
| Drying Time | 4.0 hr | ||
| Rear Temperature | 295 到 305 °C | ||
| Drying Temperature | 120 °C | ||
| Front Temperature | 320 到 330 °C | ||
| Back Pressure | 0.200 到 0.300 Mpa | ||
| Mold Temperature | 80 到 110 °C | ||
| Screw Speed | 30 到 60 rpm |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4534 BK |
|---|---|---|---|
| Modeling Shrinkage | 流动 : 24小时 | ASTM D955 | 0.30 到 0.50 % |
| Moisture Absorption | 24 hr, 50% RH | ASTM D570 | 0.10 % |
| Modeling Shrinkage | 横向流动 : 24小时 | ASTM D955 | 0.30 到 0.50 % |
| 横向流量 : 24小时 | ISO 294-4 | 0.44 % | |
| 流量 : 24小时 | 0.36 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4534 BK |
|---|---|---|---|
| Tensile Elongation | 屈服 | ISO 527-2 | 2.5 % |
| Tensile Modulus | -- | ISO 527-2/1 | 6740 Mpa |
| Flexural Strength | ASTM D790, ISO 178 | 158 Mpa | |
| Specific Wear Rate | ASTM D3702 | 2.2E+7 10^-8 mm³/N·m | |
| Flexural Modulus | -- | ISO 178 | 6400 Mpa |
| Coefficient of Friction | Dynamic | ASTM D3702 | 0.51 |
| Tensile Strength | 断裂 | ISO 527-2 | 104 Mpa |
| ASTM D638 | 103 Mpa | ||
| Tensile Elongation | 2.8 % | ||
| Tensile Strength | 屈服 | ASTM D638, ISO 527-2 | 103 Mpa |
| Tensile Modulus | -- 1 | ASTM D638 | 6890 Mpa |
| Flexural Modulus | -- | ASTM D790 | 6200 Mpa |
| Tensile Elongation | 断裂 | ISO 527-2 | 2.5 % |
| 屈服 | ASTM D638 | 2.8 % | |
| Coefficient of Friction | Static | ASTM D3702 | 0.53 |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4534 BK |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 720 J/m |
| 23°C 3 | ISO 180/1U | 44 kJ/m² | |
| Instrumented Dart Impact | 23°C, Energy at Peak | ASTM D3763 | 24.0 J |
| -- | ISO 6603-2 | 6.00 J |