| thermosetting | Test Condition | Test Method | Innovative Polymers, Inc./InnoFR™ FX-8081 |
|---|---|---|---|
| Thermosetting components | 脱模时间 | 120to240 min | |
| 硬化法 | 按重量计算的混合比:100按容量计算的混合比:100 | ||
| 树脂 | 按重量计算的混合比:44按容量计算的混合比:41 |
| Uncured Properties | Test Condition | Test Method | Innovative Polymers, Inc./InnoFR™ FX-8081 |
|---|---|---|---|
| Viscosity | 固化时间(25°C) | 1.7E+02 hr | |
| GelTime | 10to15 min | ||
| 25°C4 | 1.9 Pa·s | ||
| 25°C2 | 0.32 Pa·s | ||
| 25°C3 | 1.9 Pa·s |
| Cured Properties | Test Condition | Test Method | Innovative Polymers, Inc./InnoFR™ FX-8081 |
|---|---|---|---|
| tear strength | ASTM D624 | 23.6 kN/m | |
| elongation | 断裂 | ASTM D638 | 150 % |
| tensile strength | ASTM D638 | 7.24 MPa | |
| Shore hardness | ShoreA | ASTM D2240 | 75to85 |
| physical property | Test Condition | Test Method | Innovative Polymers, Inc./InnoFR™ FX-8081 |
|---|---|---|---|
| density | Hardener | 1.22 g/cm³ | |
| 基体树脂 | 1.30 g/cm³ | ||
| Cured | 1.30 g/cm³ | ||
| Shrinkage rate | MD | ASTM D2566 | 0.10to0.50 % |